Aluminum Strips for Radiators/Condensers/Evaporators /Heat Exchanger Using

• Application: Transportation Tools, Heat Sink, Radiators/Condensers/Evaporators /Heat Exchanger
• Certification: ISO9001, ASTM, JIS, GB, EN, ASTMB
• Technique: According to Customer′s Requirement
• Grade: According to Customer′s Requirement
• Temper: O - H112
• Surface Treatment: Coated
• Model NO.: fin strip3003, 1060, 1100, and 3003 clad 4343/4045
• Alloy: Alloy
• Type: Aluminum Strips
• Shape: Rolls
• Transport Package: Wooden Standard Packing
• Specification: According To Customers′ Requirement
• Trademark: Trumony
• Origin: Jinagsu
• HS Code: 760711
• Production Capacity: 6000mt/Year

Product Description

Runfal produces aluminum strip for heat exchangers with 3003, 1060, 4343, and 3003 clad 4343 (4343+3003+4343), 3003 clad 4045 (4045+3003+4045)/(4043/3003/7072) etc.
Aluminum strip is widely used for manufacturing radiators, condensers, evaporators, heater, charge air coolers/intercoolers, engine oil coolers/transmission oil coolers.
Specification of aluminum fin strip:
1) Aluminium fin strip in coils
2) Alloy: 1060, 3003, 4343+3003+4343, etc
3) Thickness: 0.2 - 3.0mm
4) Width: 12 - 1250mm (max)
5) Temper: O, H14, H18, H22, H24, H26
6)ID.: 150mm, 200mm, 300mm, 400mm, 500mm
7)OD.: 900-1450mmm
Main mechanical property:

Alloy Code
Temper
Tensile Strength
RM(MPa)
Yield Strength RP0.2(Mpa)
Extend Ratio
A50(%)
TR-010 etc.
O
95-135*
≥ 35*
≥ 15*
H14
140-185
≥ 125
≥ 1.5
H24
140-185
≥ 125
≥ 3.0
H16
185-225
≥ 160
≥ 1.0
H18
≥ 185
-
≥ 0.5
TR-166 etc. Tube material
H24
185-235
≥ 150
≥ 8
TR-116 etc. Tube material
H14
140-185
≥ 125
≥ 3
H24
140-185
≥ 125
≥ 8

Number	Inspection Item		Test according to
1	Raw & auxiliary materials testing	Alloy, specification	Raw & auxiliary materials testing standard HX/QP8.2.4-1-2012
		Surface quality
2	Casting	Chemical composition	Chemical composition of aluminum alloy (inner quality standard) HX/QP8.2.4-9-2007
3	Saw-cutting	Size	Aluminum alloy ingot inspection standard                        HX/QP8.2.4-2-2007
		Surface quality	Aluminum alloy ingot inspection standard                        HX/QP8.2.4-2-2007
4	Milling surface	Size	Aluminum alloy ingot after milling surface inspection standard              HX/QP8.2.4-10-2009»
		Surface quality	Aluminum alloy ingot after milling surface inspection standard               HX/QP8.2.4-10-2009
5	Welding	Size	Skin & core materials welding inspection standard HX/QP8.2.4-9-2009
		Welding quality	Skin & core materials welding inspection standard HX/QP8.2.4-9-2009
6	Heating	Temperature & time	Pusher-type aluminum sheet & ingot heating furnace operating standard             HX/QP7.5.1-1-6-2007
7	Hot-rolling	Emulsion quality	Hot-rolling emulsion inspection standard HX/QP8.2.4-4-2007
		Size	Hot-rolling materials inspection standard HX/QP8.2.4-3-2007
		Surface quality	Hot-rolling materials inspection standard HX/QP8.2.4-3-2007
8	Cold rough-rolling	Thickness	Aluminum (cladded) strip & sheet & foil products inspection standard HX/QP8.2.4-7-2011
		Rolling oil quality	Cold-rolling procustion process lubricant inspection standard HXQP8.2.4-5-2007
		Surface quality	Aluminum (cladded) strip & sheet & foil products inspection standard HX/QP8.2.4-7-2011
9	Cold finished-rolling	Thickness	Aluminum (cladded) strip & sheet & foil products inspection standard HX/QP8.2.4-7-2011
		Surface quality	Aluminum (cladded) strip & sheet & foil products inspection standard HX/QP8.2.4-7-2011
		Rolling oil quality	Cold-rolling procustion process lubricant inspection standard HXQP8.2.4-5-2007
10	Tension-levelling	Surface quality	Aluminum (cladded) strip & sheet & foil products inspection standard HX/QP8.2.4-7-2011