Aluminium Fin Stock for Air Conditioning/Aluminum Foil

• Customization: Available
• Type: Roll
• Thickness: 0.08mm-0.2mm
• Model NO.: 8011
• Foil Temper: H22,H24,H26
• Width: 50mm-1070mm
• Transport Package: According to Customer′s Request
• Specification: According to customer′s request
• Trademark: TRUMONY
• Origin: Jiangsu, China
• HS Code: 7607
• Production Capacity: 80000tons/Year

Product Description

Type: Bare, hydrophilic ( white, blue, gold)
Alloy: 1100, 1200, 8011, 3003, 1030B
Temper: H22 H24 H26 O
Thickness(mm): 0.080-0.20
Width (mm): 50-1070
Core I. D.: Φ 75, Φ 150, Φ 200, Φ 300

No. Item index Technique index
1 Film thickness 1.0~2.0um (Single side average thickness)
2 Hydrophilicity Primary contact angle Primary contact angle≤ 10°
Continuous contact Continuous contact≤ 30°
3 Anderence strength Erichson test(press deeply to 5mm): No peeling
Gridding test(100/100): No plunger separation
4 Corrosion resistance Salt spray test(72 hours)
5 Alkali resistance Dipped in 30% NaOH in 30C for 3 minutes,
Absolutely no blister
6 Impregnant resistance Sample weight loss 1%
7 Heat resistance Under 300C, for 5 minutes, performance and
Colour unchanged
Under 300Cfor 5 minutes, the coating film
Becomes a little yellow
8 Oil proof DIP in volatile oil for 24 hour,
No blisters on the coating film
9 Odor of the coating film No order
10 Abrasion to mould Same as ordinary aluminium foi.
 

		,%
		Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn		Ti	Zr			AI
1	1A99	0.003	0.003	0.005	-	-	-	-	-	-	-	-	0.02	-	99.99
2	1A97	0.015	0.015	0.005	-	-	-	-	-	-	-	-	0.005	-	99.97
3	1A95	0.03	0.03	0.01	-	-	-	-	-	-	-	-	0.005	-	99.95
4	1A93	0.04	0.04	0.01	-	-	-	-	-	-	-	-	0.007	-	99.93
5	1A90	0.06	0.06	0.01	-	-	-	-	-	-	-	-	0.01	-	99.9
6	1A85	0.08	0.1	0.01	-	-	-	-	-	-	-	-	0.01	-	99.85
7	1A80	0.15	0.15	0.03	0.02	0.02	-	-	0.03	Ca:0.03;V:0.05	0.03	-	0.02	-	99.8
8	1A80A	0.15	0.15	0.03	0.02	0.02	-	-	0.06	Ca:0.03	0.02	-	0.02	-	99.8
9	1070	0.2	0.25	0.04	0.03	0.03	-	-	0.04	V:0.05	0.03	-	0.03	-	99.7
10	1070A	0.2	0.25	0.03	0.03	0.03	-	-	0.07	-	0.03	-	0.03	-	99.7
11	1370	0.1	0.25	0.02	0.01	0.02	0.01	-	0.04	Ca:0.03;V+Ti:0.02	-	-	0.02	0.1	99.7
										B:0.02
12	1060	0.25	0.35	0.05	0.03	0.03	-	-	0.05	V:0.05	0.03	-	0.03	-	99.6
13	1050	0.25	0.4	0.05	0.05	0.05	-	-	0.05	V:0.05	0.03	-	0.03	-	99.5
14	1050A	0.25	0.4	0.05	0.05	0.05	-	-	0.07	-	0.05	-	0.03	-	99.5
15	1A50	0.3	0.3	0.01	0.05	0.05	-	-	0.03	Fe+Si:0.45	-	-	0.03	-	99.5
16	1350	0.1	0.4	0.05	0.01	-	0.01	-	0.05	Ca:0.03;V+Ti:0.02	-	-	0.03	0.1	99.5
										B:0.05
17	1145	Si+Fe:0.55		0.05	0.05	0.05	-	-	0.05	V:0.05	0.03	-	0.03	-	99.45
18	1035	0.35	0.6	0.1	0.05	0.05	-	-	0.1	V:0.05	0.03	-	0.03	-	99.35
19	1A30	0.10-0.20	0.15-0.30	0.05	0.01	0.01	-	0.01	0.02	-	0.02	-	0.03	-	99.3
20	1100	Si+Fe:0.95	-	0.2	0.05	-	-	-	0.1		-	-	0.05	0.15	99
21	1200	Si+Fe:1.00	-	0.05	0.05	-	-	-	0.1	-	0.05	-	0.05	0.15	99
22	1235	Si+Fe:0.65	-	0.05	0.05	0.05	-	-	0.1	V:0.05	0.06	-	0.03	-	99.35
23	2A01	0.5	0.5	2.2-3.0	0.2	0.20-0.50	-	-	0.1	-	0.15	-	0.05	0.1
24	2A2	0.3	0.3	2.6-3.2	0.45-0.7	2.0-2.4	-	-	0.1	-	0.15	-	0.05	0.1
25	2A04	0.3	0.3	3.2-3.7	0.50-0.8	2.1-2.6	-	-	0.1	Be:0.001-0.01	0.05-0.40	-	0.05	0.1
26	2A06	0.5	0.5	3.8-4.3	0.50-1.0	1.7-2.3	-	-	0.1	Be:0.001-0.05	0.03-0.15	-	0.05	0.1
27	2A10	0.25	0.2	3.9-4.5		0.15-0.30	-	-	0.1	-	0.15	-	0.05	0.1
28	2A11	0.7	0.7	3.8-4.8		0.40-0.8	-	0.1	0.3	Fe+Ni:0.7	0.15	-	0.05	0.1
29	2B11	0.5	0.5	3.8-4.5		0.40-0.8	-	-	0.1	-	0.15	-	0.05	0.1
30	2A12	0.5	0.5	3.8-4.9		1.2-1.8	-	0.1	0.3	Fe+Ni:0.5	0.15	-	0.05	0.1
31	2B12	0.5	0.5	3.8-4.5	0.30-0.7	1.2-1.6	-	-	0.1	-	0.15	-	0.05	0.1
32	2A13	0.7	0.6	4.0-5.0	-	0.3-0.50		-	0.6	-	0.15	-	0.05	0.1
33	2A14	0.6-1.2	0.7	3.9-4.8	0.40-1.0	0.40.0.8		0.1	0.3	-	0.15	-	0.05	0.1
34	2A16	0.3	0.3	6.0-7.0	0.40-0.8	0.05	-	-	0.1	-	0.10-0.20	0.2	0.05	0.1
35	2B16	0.250.30
5.8-6.8	0.20-0.40	0.05	-	-	-	V:0.05-0.15	0.08-0.20	0.10-0.25	0.05	0.1		-
36	2A17	0.3	0.3	6.0-7.0	0.40-0.8	0.25-0.45	-	-	0.1	-	0.10-0.20	-	0.05	0.1
37	2A20	0.2	0.3	5.8-6.8	-	0.02	-	-	0.1	V:0.05-0.15	0.07-0.16	0.10-0.25	0.05	0.15
										B:0.001-0.01
38	2A21	0.2	0.20-0.6	3.0-4.0	0.05	0.8-1.2	-	1.8-2.3	0.2	-	0.05	-	0.05	0.15
39	2A25	0.06	0.06	3.6-4.2	0.50-0.7	1.0-1.5	-	0.06	-	-	-	-	0.05	0.15
40	2A49	0.25	0.8-1.2	3.2-3.8	0.30-0.6	1.8-2.2	-	0.8-1.2	-	-	0.08-0.12	-	0.05	0.15
41	2A50	0.7-1.2	0.7	1.8-2.6	0.40-0.8	0.40-0.8	-	0.1	0.3	Fe+Ni:0.7	0.15	-	0.05	0.15
42	2B50	0.7-1.2	0.7	1.8-2.6	0.40-0.8	0.40-0.8	0.01-0.20	0.1	0.3	Fe+Ni:0.7	0.02-0.10	-	0.05	0.15
43	2A70	0.35	0.9-1.5	1.9-2.5	0.2	1.4-1.8	-	0.9-1.5	0.3	-	0.02-0.10	-	0.05	0.15
44	2B70	0.25	0.9-1.4	1.8-2.7	0.2	1.2-1.8	-	0.8-1.4	0.15	Pb:0.05;Sn:0.05	0.1	-	0.05	0.15
										Ti+Zr:0.20
45	2A80	0.50-1.2	1.0-1.6	1.9-2.5	0.2	1.4-1.8	-	0.9-1.5	0.3	-	0.15	-	0.05	0.1
46	2A90	0.05-1.0	0.50-1.0	3.5-4.5	0.2	0.40-0.8	-	1.8-2.3	0.3	-	0.15	-	0.05	0.1
47	2004	0.2	0.2	5.5-6.5	0.1	0.5	,	-	0.1	-	0.05	0.30-0.50	0.05	0.15
							-
48	2011	0.4	0.7	5.0-6.0	-	-	-	-	0.3	Bi:0.20-0.6	-	-	0.05	0.15
										Pb:0.20-0.6
49	2014	0.50-1.2	0.7	3.9-5.0	0.40-1.2	0.20-0.8	0.1	-	0.25	-	0.15	-	0.05	0.15
50	2014A	0.50-0.9	0.5	3.9-5.0	0.40-1.2	0.20-0.8	0.1	0.1	0.25	Ti+Zr:0.02	0.15	-	0.05	0.15
51	2214	0.50-1.2	0.3	3.9-5.0	0.40-1.2	0.20-0.8	0.1	-	0.25	-	0.15	-	0.05	0.15
52	2017	0.20-0.8	0.7	3.5-4.5	0.40-1.0	0.40-0.8	0.1	-	0.25	-	0.15	-	0.05	0.15
53	2017A	0.20-0.8	0.7	3.5-4.5	0.40-1.0	0.40-1.0	0.1	-	0.25	Ti+Zr:0.25	-	-	0.05	0.15
54	2117	0.8	0.7	2.2-3.0	0.2	0.20-0.50	0.1	-	0.25	-	-	-	0.05	0.15
55	2218	0.9	1	3.5-4.5	0.2	1.2-1.8	0.1	1.7-2.3	0.25	-	-	-	0.05	0.15
56	2618	0.19-0.25	0.9-1.3	1.9-2.7	-	1.3-1.8	-	0.9-1.2	0.1	-	0.04-0.10	-	0.05	0.15
57	2219	0.2	0.3	5.8-6.8	0.20-0.40	0.02	-	-	0.1	V:0.05-0.15	0.20-0.10	0.10-0.25	0.05	0.15
58	2024	0.5	0.5	3.8-4.9	0.30-0.9	1.2-1.8	0.1	-	0.25	-	0.15	-	0.05	0.15
59	2124	0.2	0.3	3.8-4.9	0.30-0.9	1.2-1.8	0.1	-	0.25	-	0., 15<, /P>	-	0.05	0.15
60	3A21	0.6	0.7	0.2	1.0-1.6	0.05	-	-	0.10	-	0.15	-	0.05	0.15
61	3003	0.6	0.7	0.05-0.20	1.0-1.5	-	-	-	0.1	-	-	-	0.05	0.15		-
62	3103	0.5	0.7	0.1	0.9-1.5	0.3	0.1	-	0.2	Ti+Zr:0.10	-	-	0.05	0.15		-
63	3004	0.3	0.7	0.25	1.0-1.5	0.8-1.3	-	-	0.25	-	-	-	0.05	0.15		-
64	3005	0.6	0.7	0.3	1.0-1.5	0.20-0.6	0.1	-	0.25	-	0.1	-	0.05	0.15		-
65	3105	0.6	0.7	0.3	0.30-0.8	0.20-0.8	0.2	-	0.4	-	0.1	-	0.05	0.15		-
66	4A01	4.5-6.0	0.6	0.2	-	-	-	-	Zn+Sn:	-	0.15	-	0.05	0.15		LT1
									0.1
67	4A11	11.5-13.5	1	0.50-1.3	0.2	0.8-1.3	0.1	0.50-1.3	0.25	-	0.15	-	0.05	0.15		LD11
68	4A13	6.8-8.2	0.5	Cu+Zn:	0.5	0.05	-	-	-	Ca:0.10	0.15	-	0.05	0.15		LT13
				0.15
69	4A17	11.0-12.5	0.5	Cu+Zn:	0.5	0.05	-	-	-	Ca:0.10	0.15	-	0.05	0.15		LT17
				0.15
70	4004	9.0-10.5	0.8	0.25	0.1	1.0-2.0	-	-	0.2	-	-	-	0.05	0.15		-
71	4032	11.0-13.5	1	0.50-1.3	-	0.8-1.3	0.1	0.50-1.3	0.25	-	-	-	0.05	0.15		-
72	4043	4.5-6.0	0.8	0.3	0.05	0.05	-	-	0.1	-	0.2	-	0.05	0.15		-
73	4043A	4.5-6.0	0.6	0.3	0.15	0.2	-	-	0.1	-	0.15	-	0.05	0.15		-
74	4047	11.0-13.0	0.8	0.3	0.15	0.1	-	-	0.2	-	-	-	0.05	0.15		-
75	4047A	11.0-13.0	0.6	0.3	0.15	-	-	-	0.2	-	0.15	-	0.05	0.15		-
76	5A01	Si+Fe:0.40		0.1	0.30-0.7	6.0-7.0	0.10-0.20	-	0.25	-	0.15	0.10-0.20	0.05	0.15		LF15
77	5A02	0.4	0.4	0.1	Cr	2.0-2.8	-	-	-	Si+Fe:0.6	0.15	-	0.05	0.15		LF2
					0.15-0.40
78	5A03	0.50-0.8	0.5	0.1	0.30-0.6	3.2-3.8	-	-	0.2	-	0.15	-	0.05	0.15		LF3
79	5A05	0.5	0.5	0.1	0.30-0.6	4.8-5.5	-	-	0.2	-	-	-	0.05	0.15		LF5
80	5B05	0.4	0.4	0.2	0.20-0.6	4.7-5.7	-	-	-	Si+Fe:0.6	0.15	-	0.05	0.15		LF10
81	5A06	0.4	0.4	0.1	0.50-0.8	5.8-6.8	-	-	0.2	Be:0.0001-0.005	0.02-0.10	-	0.05	0.15		LF6
82	5B06	0.4	0.4	0.1	0.50-0.8	5.8-6.8	-	-	0.2	Be:0.0001-0.005	0.10-0.30	-	0.05	0.15		LF14
83	5A12	0.3	0.3	0.05	0.4-0.8	8.3-9.6	-	0.1	0.2	Be:0.005	0.05-0.15	-	0.05	0.15		LF12
										Sb:0.004-0.05
84	5A13	0.3	0.3	0.05	0.40-0.8	9.2-10.5	-	0.1	0.2	Be:0.005	0.05-0.15	-	0.05	0.15		LF13
										Sb:0.004-0.05
85	5A30	Si+Fe:0.40		0.1	0.50-1.0	4.7-5.5	-	-	0.25	Cr:0.05-0.20	0.03-0.15		0.05	0.15		LF16
86	5A33	0.35	0.35	0.1	0.1	6.0-7.5	-	-	0.50-1.5	Be:0.0005-0.005	0.05-0.15	0.10-0.30	0.05	0.15		LF33
87	5A41	0.4	0.4	0.1	0.30-0.6	6.0-7.0	-	-	0.2	-	0.02-0.10	-	0.05	0.15		LT41
88	5A43	0.4	0.4	0.1	0.15-0.40	0.6-1.4	-	-	-	-	0.15	-	0.05	0.15		LF43
89	5A66	0.005	0.01	0.005	-	1.5-2.0	-	-	-	-	-	-	0.05	0.15		LT66
90	5005	0.3	0.7	0.2	0.2	0.50-1.1	0.1	-	0.25	-	-	-	0.05	0.15		-
91	5019	0.4	0.5	0.1	0.10-0.6	4.5-5.6	0.2	-	0.2	Mn+Cr:0.10-0.6	0.2	-	0.05	0.15		-
92	5050	0.4	0.7	0.2	0.1	1.1-1.8	0.1	-	0.25	-	-	-	0.05	0.15		-
93	5251	0.4	0.5	0.15	0.10-0.50	1.7-2.4	0.15	-	0.15	-	0.15	-	0.05	0.15		-
94	5052	0.25	0.4	0.1	0.1	2.2-2.8	0.15-0.35	-	0.1	-	-	-	0.05	0.15		-
95	5154	0.25	0.4	0.1	0.1	3.1-3.9	0.15-0.35	-	0.2	-	0.2	-	0.05	0.15		-
96	5154A	0.5	0.5	0.1	0.5	3.1-3.9	0.25	-	0.2		0.2	-	0.05	0.15		-
										Mn+Cr:0.10-0.50
97	5454	0.25	0.4	0.1	0.50-1.0	2.4-3.0	0.05-0.20	-	0.25	-	0.2	-	0.05	1.15		-
98	5554	0.25	0.4	0.1	0.50-1.0	2.4-3.0	0.05-0.20	-	0.25	-	0.05-0.20	-	0.05	0.15		-
99	5754	0.4	0.4	0.1	0.5	2.6-3.6	0.3	-	0.2	Mn+Cr:0.10-0.60	0.15	-	0.05	0.15		-
100	5056	0.3	0.4	0.1	0.05-0.20	4.5-5.6	0.05-0.20	-	0.1	-	-	-	0.05	0.15		LF5-1
101	5356	0.25	0.4	0.1	0.05-0.20	4.5-5.5	0.05-0.20	-	0.1	-	0.06-0.20	-	0.05	0.15		-
102	5456	0.25	0.4	0.1	0.50-1.0	4.7-5.5	0.05-0.20	-	0.25	-	0.2	-	0.05	0.15		-
103	5082	0.2	0.35	0.15	0.15	4.0-5.0	0.15	-	0.25	-	0.1	-	0.05	0.15		-
104	5182	0.2	0.35	0.15	0.20-0.50	4.0-5.0	0.1	-	0.25	-	0.1	-	0.05	0.15		-
105	5083	0.4	0.4	0.1	0.40-1.0	4.0-4.9	0.05-0.25	-	0.25	-	0.15	-	0.05	0.15		LF4
106	5183	0.4	0.4	0.1	0.50-1.0	4.3-5.2	0.05-0.25	-	0.25	-	0.15	-	0.05	0.15		-
107	5086	0.4	0.5	0.1	0.20-0.7	3.5-4.5	0.05-0.25	-	0.25	-	0.15	-	0.05	0.15		-
108	6A02	0.50-1.2	0.5	0.20-0.6	Cr	0.45-0.9	-	-	0.2	-	0.15	-	0.05	0.1		LD2
					0.15-0.35
109	6B02	0.7-1.1	0.4	0.10-0.40	0.10-0.30	0.40-0.8	-	-	0.15	-	0.01-0.04	-	0.05	0.1		LD2-1
110	6A51	0.50-0.7	0.5	0.15-0.35	-	0.45-0.6	-	-	0.25	Sn:0.15-0.35	0.01-0.04	-	0.05	0.15		-
111	6101	0.30-0.7	0.5	0.1	0.03	0.35-0.8	0.03	-	0.1	B:0.06	-	-	0.03	0.1		-
112	6101A	0.30-0.7	0.4	0.05	-	0.40-0.9	-	-	-	-	-	-	0.03	0.1		-
113	6005	0.6-0.9	0.35	0.1	0.1	0.40-0.6	0.1	-	0.1	-	0.1	-	0.05	0.15		-
114	6005A	0.50-0.9	0.35	0.3	0.5	0.40-0.7	0.3	-	0.2	Mn+Cr:0.12-0.50	0.1	-	0.05	0.15		-
115	6351	0.7-1.3	0.5	0.1	0.40-0.8	0.40-0.8		-	0.2	-	0.2	-	0.05	0.15		-
116	6060	0.30-0.6	0.10-0.30	0.1	0.1	0.35-0.6	0.05	-	0.15	-	0.1	-	0.05	0.15		-
117	6061	0.40-0.8	0.7	0.15-0.40	0.15	0.8-1.2	0.04-0.35	-	0.25	-	0.15	-	0.05	0.15		LD30
118	6063	0.20-0.6	0.35	0.1	0.1	0.45-0.9	0.1	-	0.1	-	0.1	-	0.05	0.15		LD31
119	6063A	0.30-0.6	0.15-0.35	0.1	0.15	0.6-0.9	0.05	-	0.15	-	0.1	-	0.05	0.15		-
120	6070	1.0-1.7	0.5	0.15-0.40	0.40-1.0	0.50-1.2	0.1	-	0.25	-	0.15	-	0.05	0.15		LD2-2
121	6181	0.8-1.2	0.45	0.1	0.15	0.6-1.0	0.1	-	0.2	-	0.1	-	0.05	0.15		-
122	6082	0.7-1.3	0.5	0.1	0.40-1.0	0.6-1.2	0.25	-	0.2	-	0.1	-	0.05	0.15		-
123	7A01	0.3	0.3	0.01	-	-	-	-	0.9-1.3	Si+Fe:0.45	-	-	0.03	-		LB1
124	7A03	0.2	0.2	1.8-2.4	0.1	1.2-1.6	0.05	-	6.0-6.7	-	0.02-0.08	-	0.05	0.1		LC3
125	7A04	0.5	0.5	1.4-2.0	0.20-0.6	1.8-2.8	0.10-0.25	-	5.0-7.0	-	0.1	-	0.05	0.1		LC4
126	7A05	0.25	0.25	0.2	0.15-0.40	1.1-1.7	0.05-0.15	-	4.4-5.0	-	0.02-0.06	0.10-0.25	0.05	0.15		-
127	7A09	0.5	0.5	1.2-2.0	0.15	2.0-3.0	0.16-0.30	-	5.1-6.1	-	0.1	-	0.05	0.1		LC9
128	7A10	0.3	0.3	0.50-1.0	0.20-0.35	3.0-4.0	0.10-0.20	-	3.2-4.2	-	0.1	-	0.05	0.1		LC10
129	7A15	0.5	0.5	0.50-1.0	0.10-0.40	2.4-3.0	0.10-0.30	-	4.4-5.4	Be:0.005-0.01	0.05-0.15	-	0.05	0.15		LC15
130	7A19	0.3	0.4	0.08-0.30	0.30-0.50	1.3-1.9	0.10-0.20	-	4.5-5.3	Be:0.0001-0.004	-	0.08-0.20	0.05	0.15		LC19
131	7A31	0.3	0.6	0.10-0.40	0.20-0.40	2.5-3.3	0.10-0.20	-	3.6-4.5	Be:0.0001-0.001	0.02-0.10	0.08-0.25	0.05	0.15		-
132	7A33	0.25	0.3	0.25-0.55	0.05	2.2-2.7	0.10-0.20	-	4.6-5.4	-	0.05	-	0.05	0.1		-
133	7A52	0.25	0.3	0.05-0.20	0.20-0.50	2.0-2.8	0.15-0.25	-	4.0-4.8	-	0.05-0.18	0.05-0.15	0.05	0.15		LC52
134	7003	0.3	0.35	0.2	0.3	0.50-1.0	0.2	-	5.0-6.5	-	0.2	0.05-0.25	0.05	0.15		LC12
135	7005	0.35	0.4	0.1	0.20-0.7	1.0-1.8	0.06-0.20	-	4.0-5.0	-	0.10-0.06	0.08-0.20	0.05	0.15		-
136	7020	0.35	0.4	0.2	0.05-0.50	1.0-1.4	0.10-0.35	-	4.0-5.0	Zr+Tr:0.08-0.25	-	0.08-0.20	0.05	0.15		-
137	7022	0.5	0.5	0.50-1.0	0.10-0.40	2.6-3.7	0.10-0.30	-	4.3-5.2	Zr+Tr:0.02	-	-	0.05	0.15		-
138	7050	0.12	0.15	2.0-2.6	0.1	1.9-2.6	0.04	-	5.7-6.7	-	0.06	0.08-0.15	0.05	0.15		-
139	7075	0.4	0.5	1.2-2.0	0.3	2.1-2.9	0.18-0.28	-	5.1-6.1	-	0.2	-	0.05	0.15		-
140	7475	0.1	0.12	1.2-1.9	0.06	1.9-2.6	0.18-0.25	-	5.2-6.2	-	0.06	-	0.05	0.15		-
141	8A06	0.55	0.5	0.1	0.1	0.1	-	-	0.1	Fe+Si:1.0	-	-	0.05	0.15		L6
142	8011	0.50-0.9	0.6-1.0	0.1	0.2	0.05	0.05	-	0.1	-	0.08	-	0.05	0.15
143	8090	0.2	0.3	1.0-1.6	0.1	0.6-1.3	0.1	-	0.25	Li:2.2-2.7	0.1	0.04-0.16	0.05	0.15